Ion-implanted layers with abrupt edges

ABSTRACT

A structure in the form of an ion-implanted layer with asymmetric edges is formed in a semiconductor substrate. The asymmetric edge has one end which slopes toward the surface of the substrate and the other which terminates abruptly inside the bulk of the substrate. The structure is formed using lift-off techniques to make ion-stopping masks with near-vertical sidewalls which delineate the abrupt edges of the ion-implanted layers. The application of this structure to fabricate Schottky barrier FET&#39;s and bipolar transistors yields devices with reduced parasitic resistance without adversely impacting other related electrical parameters such as breakdown voltage and capacitance.

This is a continuation of application Ser. No. 760,788 filed Jan. 19, 1977, which is a division of application Ser. No. 701,375, filed June, 30, 1976, now U.S. Pat. No. 4,029,522.

FIELD OF THE INVENTION

The invention disclosed relates to semiconductor fabrication processes and devices and more particularly to an ion-implantation process and the resulting semiconductor product.

BACKGROUND OF THE INVENTION

High performance Schottky barrier FET's and bipolar transistors have active regions in the bulk of a semiconductor body thus avoiding the deleterious effects of surface discontinuities on carrier mobilities. On the other hand, to make possible large scale integration, it is necessary to bring the active bulk regions of the device in contact with the top surface of the structure. In doing this, parasitic resistive and capacitive elements are created which degrade the high performance of the bulk device. Compromises between resistive and capacitive parasitics are difficult to achieve since increasing or decreasing the doping to minimize one of them, respectively, adversely impacts the other. Moreover, doping levels are generally determined by the design of bulk devices.

The performance obtained from conventionally fabricated Schottky barrier FET's is limited by:

(1) High source-gate and drain-gate parasitic resistance,

(2) High interelectrode capacitance, and

(3) Low interelectrode breakdown voltage.

For bipolar transistors the problems include:

(1) High extrinsic base resistance,

(2) Low base-emitter breakdown voltage,

(3) High base-emitter sidewall capacitance and

(4) Self-biasing along the emitter width, a deleterious effect known as emitter crowding.

OBJECTS OF THE INVENTION

It is therefore an object of the invention to fabricate high performance semiconductor devices in an improved manner.

It is another object of the invention to build high performance semiconductor devices in the bulk of the semiconductor medium in an improved manner.

It is still a further object of the invention to build a high performance semiconductor device in the bulk of the semiconductor medium with reduced capacitive and resistive parasitic elements.

It is still a further object of the invention to build a high performance Schottky barrier FET device with reduced source-gate region and drain-gate region parasitic resistance.

It is still a further object of the invention to build a high performance Schottky barrier FET device with reduced interelectrode capacitance.

It is still a further object of the invention to build a high performance Schottky barrier FET device with higher interelectrode breakdown voltage.

It is still a further object of the invention to build a high performance bipolar transistor device with a reduced extrinsic base resistance.

It is still a further object of the invention to build a high performance bipolar device with reduced emitter crowding effect.

SUMMARY OF THE INVENTION

These and other objects, features and advantages are accomplished by the process and device invention disclosed herein.

The inventive process forms asymmetrical, buried, high conductance layers in the semiconductor bulk. It comprises steps including forming a first oxide layer on the surface of the semiconductor substrate, having an opening with tapered sidewalls and the portion of the substrate surface exposed through the opening covered by one or more dielectric layers whose total thickness is less than that of the first layer. Then depositing a layer of a lift-off resist and exposing the resist so as to delineate a first region with one edge inside the opening in the first layer and the opposite edge overlapping one of the tapered sidewalls. Then removing the resist from the first region and depositing a layer of ion-beam stopping material. Next, the remaining portion of the resist layer is removed which simultaneously lifts off the ion-stopping layer above it. The remaining ion-stopping layer constitutes a mask with near-vertical sidewalls. A blanket implant follows which penetrates the unmasked portion of the first layer's opening. There results a high conductance layer formed in the bulk of the substrate having a first end substantially following the contour of one of the tapered sidewalls of the first layer so as to contact the surface of the substrate and a second end abruptly terminating within the bulk of the substrate and aligned with respect to the edge of the ion-stopping mask.

The method permits the fabrication of asymmetrical buried layers with abrupt edges. The lift-off technique is used to fabricate a mask with near-vertical sidewalls which delineate the abrupt edges of the buried layers. The introduction of this method into fabrication processes for Schottky barrier FET's and bipolar transistors yields devices with improved electrical characteristics. For the Schottky barrier FET, the improvements include a reduced source-gate region and drain-gate region parasitic resistance, a reduced interelectrode capacitance, a larger interelectrode breakdown voltage, and a gate self-aligned with respect to the buried layers. For bipolar transistors, the improvements include a reduced extrinsic base resistance without lowering the base-emitter breakdown voltage or increasing the base-emitter sidewall capacitance, a channel stopper in the base region and a reduction of the emitter crowding effect.

DESCRIPTION OF THE FIGURES

These and other objects, features and advantages of the invention can be more fully appreciated with reference to the accompanying drawings.

FIG. 1 illustrates a cross-sectional view of the semiconductor structure after the window 6 is delineated in the oxide layer 4.

FIG. 2a shows a prior art polymethyl methacrylate (PMM) resist with vertical sidewalls.

FIG. 2b shows a prior art PMM resist lift-off technique.

FIG. 3 shows the formation of a window 24 in a lift-off resist 22 with a vertical sidewall 26.

FIG. 4 shows layers of lift-off resist 22 and of ion-stopping material 30 suitable for the lift-off technique.

FIG. 5 shows an ion-implanted, asymmetric buried layer.

FIG. 6a shows a prior art Schottky barrier FET with a low resistance zone embedded in the substrate and parasitic resistance between said substrate and source/drain contacts.

FIG. 6b shows a prior art Schottky barrier FET with low resistance zones on top of the conductive layer.

FIG. 7 shows a cross-section of a Schottky barrier FET after implantation of buried layers.

FIG. 8 shows the structure of FIG. 7 after growth of recessed oxide.

FIG. 9 shows a cross-section of the finished Schottky barrier FET with asymmetrical buried layers.

FIG. 10 illustrates the formation of oxide isolation regions surrounding the pocket where a bipolar transistor will be fabricated.

FIG. 11 shows tapered oxide sidewalls forming the base window for the structure of FIG. 10.

FIG. 12 shows the structure of FIG. 11 after implantation of the base region and opening of the window for the collector contact.

FIG. 13 shows the structure of FIG. 12 after exposing and developing lift-off resist to make windows with near-vertical sidewalls.

FIG. 14 shows the structure of FIG. 13 with windows etched out of the Si₃ N₄ layer through which the emitter and collector contact are implanted.

FIG. 15 shows the structure of FIG. 14 with a polysilicon mask in place over the emitter and collector contact.

FIG. 16 shows the structure of FIG. 15 with the polysilicon layer enlarged after its oxidation.

FIG. 17 shows the structure of FIG. 16 after implantation of asymmetric buried layers in the base region.

FIG. 18 shows the structure of FIG. 17 where the polysilicon and silicon dioxide masks have been etched away.

FIG. 19 shows the completed bipolar transistor device with the buried asymmetric layers in the base region which reduce the extrinsic base resistance.

DISCUSSION OF THE PREFERRED EMBODIMENT

The prior art includes lift-off techniques for forming photolithographic masks such as that disclosed by M. Hatzakis, "Electron Resist for Microcircuit and Mask Production," J. Electrochem. Soc., Vol. 116, No. 7, July 1969, pp. 1033-1037. FIGS. 2a and 2b herein reproduce FIGS. 5a and 7 of the Hatzakis paper, showing how a semiconductor 18 can be deposited through a window in a layer of lift-off resist 12 composed of polymethyl methacrylate (PMM). The PMM is a positive acting electron-sensitive resist which forms nearly vertical sidewalls 16. After depositing the conductor or insulator layer 14 and 18, the lift-off layer 12 is dissolved away allowing layer 14 to be lifted off, leaving the layer 18 in place.

Prior art lift-off resists have not been employed in ion-implantation processes. If the lift-off resist layer 12 of FIG. 2b were, itself, used as an ion-implantation mask, buried conductive regions would be formed with all edges abruptly terminated within the bulk of the semiconductor substrate where electrical contact cannot be made to the surface. Furthermore, the buried region is not amenable to self-alignment with other device structures due to the low melting and decomposition temperatures of the lift-off resist.

One aspect of the invention disclosed herein is to employ a precise ion-implantation stopping mask formed by a lift-off technique, to delineate buried conductive regions which are abruptly terminated on one end and gradually slope toward the surface on the other end. Another aspect of the invention is to employ this ion-implantation stopping mask to also delineate additional structures in the device being fabricated, which will be self-aligned with the abruptly terminated ends of the buried conductive regions. This is accomplished as is shown in FIGS. 3, 4 and 5 wherein the lift-off resist layer 22 has at least one of its vertical sidewalls 26 located over an opening 24 in an underlying layer 4. The layer 4 has a tapered sidewall 10 covered by the lift-off resist layer 22. A layer of ion-implantation stopping material 28 and 30 is deposited over all surfaces and the lift-off resist layer 22 is then dissolved. This permits the lifting off of the layer 28 leaving sidewall 11 covered with ion-stopping layer 30 and the uncovered sidewall 10 of layer 4. A blanket ion-implantation will then result in the formation of a buried conductive region 34 having an abruptly terminated end 38 aligned with sidewall 32 and an opposite end 36 beneath sidewall 10, sloping toward the surface of substrate 2. Furthermore, the ion-stopping layer 30, which may be refractory material such as SiO₂, can itself serve as the mask for a subsequently formed self-aligned device structure such as the gate region in an FET device or an emitter contact in a bipolar transistor device.

In this disclosure a fabrication method is described to reduce parasitic resistance by means of high conductance buried layers. This layer or layers are implanted without altering the doping levels of the active regions of the device. Thus, parasitic resistances can be minimized independently of the rest of the structure. The method is quite general and its application to Schottky barrier FETs and bipolar transistors is illustrated. The essential steps of the fabrication sequence are given first. Specific applications follow.

Fabrication of Asymmetrical, High-Conductance Buried Layers

Step 1A: Start with an n-type semiconductor substrate 2 as in FIG. 1. Grow a 6000A thick SiO₂ layer 4. Deposit phospho-silicate glass (PSG) if the taper of subsequently etched oxide windows is to be less than 45 degrees.

Step 2A: Using mask #1, define and etch window 6 underneath which the desired layer is to be buried as shown in FIG. 1. Regrow SiO₂ layer 8 to a thickness of 1000A so that the magnitude of the difference in thickness between layers 4 and 8 is approximately equal to the depth of the buried layer.

FIGS. 2a and 2b illustrate prior art Hatzakis technique for the fabrication of a device structure 18 by means of a lift-off technique. This prior art technique is modified in the subject invention to produce an ion-implantation stopping mask. As described by Hatzakis, a device structure is deposited after exposing and developing windows in the lift-off resist 12. If the deposited layer 14 is thinner than the resist 12, it will not completely fill up the opening so that a gap will exist between the material 18 covering the bottom of the window and the top of the resist 12. A solvent agent can then reach the resist 12 through the gap and dissolve the unexposed resist 12, thereby lifting off the layer 14 lying on top. The deposited layer 18 will be left where the window was with near-vertical sidewalls. According to the article by M. Hatzakis, the slant of this layer 18 is between 2 to 5 degrees for a resist 12 thickness of 5000A. The important considerations for this lift-off technique are thickness of the resist layer 12 and substrate temperature during deposition of material 18. The thinner the resist 12, the closer to vertical the sidewalls 16 are.

The following steps in the subject invention include the above lift-off technique employing PMM, to produce implanted layers with asymmetrical shapes. It should be noted that other lift-off techniques can be used so long as they delineate a near vertical for ion-stopping mask.

Step 3A: Cover surface of structure in FIG. 1 with PPM resist 20 and 22 as shown in FIG. 3. Use a programmed electron beam to expose that section 24 overlapping the oxide taper 11 where a vertical mask edge 26 is needed. Develop resist to remove exposed regions. For 5000A thick resist 20, the slope of the sidewalls 26 is between 2 and 5 degrees. The thinner the resist 20, the closer the sidewall 26 to vertical.

Step 4A: Deposit material layers 28 and 30 shown in FIG. 4, thinner than the resist 20 of step 3A. Si₃ N₄ is a good material choice for the purpose of masking against ion implantation since it has a density 1.6 times larger than that of SiO₂. Consequently, 4200A of Si₃ N₄ are equivalent to 7000A of SiO₂, and the 5000A of resist 20 used in step 3A are sufficient. The substrate temperature should not exceed 100° C. during Si₃ N₄ deposition. The deposition of Si₃ N₄ layers at low temperature is reported by R. Gereth and W. Scherber in "Properties of Ammonia-Free-Nitrogen-Si₃ N₄ Films Produced at Low Temperatures," J. Electrochem. Soc., Vol. 119, No. 9, September 1972, pp. 1248-1254.

Step 5A: Lift-off PMM resist layers 20 and 22. The edge 32 of the remaining Si₃ N₄ layer 30 in FIG. 5 should be near-vertical. After the wafer is irradiated by a blanket phosphorous implant of 1×10¹⁴ ion/cm² at 450 Kev, the resulting buried layer 34 should be at a depth of 5000A with one edge 36 sloping toward the surface and the other 38 terminating abruptly underneath edge 32 of the Si₃ N₄ mask 30. The implanted impurities are activated with a low temperature anneal which will not appreciably diffuse them.

The fabrication processes for improved Schottky barrier FET and bipolar transistor incorporating these buried layers are described next.

Schottky Barrier FET with Low Source-Gate Region and Drain-Gate Region Resistance

In Drangeid, et al., "Method for Making a Schottky-Barrier Field Effect Transistor," U.S. Pat. No. 3,804,681, Apr. 16, 1974, assigned to IBM, several approaches are described to fabricate Schottky barrier FETs with low resistance zones between source and gate region to improve device transconductance and between gate region and drain to improve power dissipation and R-C time constant. These zones 40 lie in one plane at either the interface between substrate 42 and conducting layer 44 as shown in FIG. 6a, or at the top of the conducting layer 44 as in FIG. 6b.

Since in both instances of FIGS. 6a and 6b, the low resistance zone 40 is one dimensional, there is always some remaining parasitic resistance. Using the disclosed inventive technique, these remaining resistances are eliminated since the implanted buried layers slope towards the surface. A description of the fabrication steps follow:

The previously given steps 1A through 5A are carried out for a symmetrical structure appropriate for Schottky barrier FET's. At step 5A, the corresponding cross-section is shown in FIG. 7.

The Si₃ N₄ layer 46 is next utilized for a localized oxidation of the thin oxide region surrounding 46. This must be done while assuring that the implanted layers 48 and 50 diffuse as little as possible. To this end, the oxidation should be done in steam. A cycle of 1.5 hr at 900° C. yields 5500A of oxide and spreads the implant about 2000A. Another alternative is to carry out the oxidation at high pressure in order to bring down the temperature to within 700° C. The cross-sectional view of the structure with recessed oxide 52 is shown in FIG. 8. Because of the recessed oxide 52 partially fills the interelectrode space, the corresponding capacitance is reduced and the interelectrode breakdown voltage is larger than in conventionally made devices with the same geometrical dimensions. Since phosphorous piles up during the oxide growth, its concentration near the surface 54, 55 remains high. The significance of this will be discussed in connection with the fabrication of the source and drain ohmic contacts.

Step 6B: Use mask #3 in conjunction with well-known etching techniques open windows for source and drain contacts 59 and 61 of FIG. 9. The gate window does not need mask definition since it is opened by dip etching into warm phosphoric acid which selectively etches Si₃ N₄ layer 46, thus making possible self-alignment of the gate electrode 57 with respect to the abrupt edge of the buried layers. The remaining SiO₂ covering the gate is removed with a dip etch in HF. Mask #4 is used to define the pattern for the metallurgy after its deposition. Notice that due to the high impurity concentration of the layers 54 and 55 at the surface, source and drain ohmic contacts 59 and 61 are automatically established. The finished structure is shown in FIG. 9.

Bipolar Transistor with Reduced Extrinsic Base Resistance

Asymmetrical buried layers are next used to lower the extrinsic base resistance of bipolar transistors. This is the resistance between the outer edges of the active base region and the base ohmic contacts. The process is as follows.

Step 1C using mask #1: Fabrication of the structure of FIG. 10 employs mask #1 and associated etching to open a window through an oxide layer masking the starting p⁻ substrate 56. Buried layer 60 is then formed by depositing therethrough n-type impurities, such as arsenic. After stripping the masking oxide layer, n- type epitaxial layer 58 is deposited to a thickness of about one micrometer.

Step 2C: The process continues by thermally growing SiO₂ layer 62 on the epi layer 58. This oxide will be protecting the final structure and hence its thickness is determined from considerations related to oxide breakdown voltage and inversion of the p-type base region. The latter problem is eliminated by the buried layer implanted at step 12C which, among other things, acts as an inversion channel stopper. Thus, a 1000A thick layer is sufficient. Next, deposit a 500A thick layer 64 of Si₃ N₄ , which is used for a localized oxidation in step 3C and as an etch mask in step 13C. The thickness of the Si₃ N₄ layer 64 is chosen so that the polysilicon layer evaporated during step 10C does not have to be excessively thick.

Step 3C using mask #2: Use mask #2 to open windows for oxide isolation regions 68 and 70, as shown in FIG. 10. Etch SiO₂ layer 62, using the Si₃ N₄ layer 64 as an etch mask. Etch a moat into the portion of the n- epi layer defined by these windows. Grow thermal oxide 68 and 70 inside these moats until the oxide isolation is coplanar with the rest of the structure. Steps 1C through 3C are typical of the localized oxidation technique. Since the Si₃ N₄ layer 64 is a good mask against gallium, a channel stopper underneath the oxide isolation is commonly introduced by means of a blanket gallium diffusion.

Step 4C: In FIG. 11 deposit a layer 72, composed of SiO₂ and PSG. The total thickness of this layer 72 should be able to block the implant of step 12C. For the transistor under consideration, 8000A is sufficient.

Step 5C using mask #3: Use mask #3 and well-known etching techniques to open window 74 for the base dopant deposition. The tapers 76 and 78 of this window are determined by the PSG content of the layer 72 deposited at step 4C, as shown in FIG. 11.

Step 6C: Blanket implant a boron dosage of 1.6×10¹² ion/cm² at 280 Kev through SiO₂ --Si₃ N₄ layers 62 and 64. Drive-in boron to form base region 82 with its junction 80 at a depth of 6000A, as illustrated in FIG. 12. This junction will be driven deeper during step 11C.

Step 7C using mask #4: Use this mask to open window 84 for the collector contact, as shown in FIG. 12, which will be doped during the emitter deposition.

Step 8C: Cover wafer with a 7000A thick layer of positive acting, electron sensitive PPM resist 86 as shown in FIG. 13. Use an electron beam to define the emitter and collector contact windows 88 and 90, respectively. Develop and bake resist.

Step 9C: Plasma etch nitride layers 92 and 94 by reactive plasma etching techniques. Blanket implant As dose of 8×10¹⁵ /cm² at 300 Kev to form emitter region and collector contact 96 and 98, respectively in FIG. 14. For both operations, the PMM resist 86 acts as a mask. The base region directly underneath the emitter 96 is the active base region 85.

Step 10C: Evaporate a polysilicon layer over the structure of FIG. 14 keeping the substrate temperature below 100° C. After lifting off the PPM, polysilicon layers 100 and 102 of FIG. 15 are left covering the emitter 96 and collector contact 98. The polysilicon layer 100 masks the subsequent implant of the buried asymmetrical layer from compensating the emitter doping 96 and hence it should be as thick as the layers 64 and 72 combined plus a correction factor of six tenths of the thickness of the Si₃ N₄ layer 64 since the density of Si₃ N₄ is 1.6 times larger than that of silicon. For the transistor design under consideration, 6000A of polysilicon is sufficient since the SiO₂ growth of step 11C will thicken this mask to 8800A.

Step 11C: Although the lateral spread of the implanted emitter 96 is in the neighborhood of 1000A, there will be some overlap between the emitter 96 and the buried layer implant of step 12C, unless the polysilicon layer 100 masking the emitter 96 is enlarged. To accomplish this, a thermal cycle is used to grow a SiO₂ layer 104 on the sidewalls of the polysilicon layer 100 masking the emitter 96 as shown in FIG. 16. This growth should be of the order of 2800A. It may reduce the sharpness of the edges of the initial polysilicon 100, however, with the enlarged mask over the emitter 96, the need for steep mask edges to produce a buried layer with an abrupt edge is less important. Since polysilicon layer 102 is also exposed, its surface is also oxidized to produce a similar SiO₂ layer 106 which, however, serves no practical purpose. This thermal cycle will also drive-in the emitter 96 and anneal its ion-implanted damage.

Step 12C: Blanket implant a boron dosage of 5×10¹³ ion/cm² at 320 Kev to a depth of 6000A to get asymmetrical buried layers 108 and 110, which intercept the base 82 surface as shown in FIG. 17. Anneal the damage due to ion implantation with a 20 minute 900° C. heat cycle.

Step 13C: Dip etch in HF to remove SiO₂ layers 72, 104 and 106. The tapered portion of the layer 72 around the collector contact is not completely removed since it is masked by the polysilicon layer 102. Thus, after dipping in a solution of hydrofluoric and nitric acids to etch layers 100 and 102, a SiO₂ mound 102' is left over as shown in FIG. 18.

Step 14C using masks #5, #6 and #7: Use mask #5 and well known etching techniques to open contact holes to the emitter 96 and collector 98 as shown in FIG. 19. Mound 102' will also be removed during this etching operation by making the size of the collector contact sufficiently large. Alignment of mask #5 to emitter 96 is not critical since the window etched in the Si₃ N₄ layer 64 at step 9C confines the etching of the contact hole to be within the emitter region. The Si₃ N₄ layer 64 is next removed by dip etching in warm phosphoric acid. Mask #6 and well known etching operations are then used to open the contact hole for the base region 82. After deposition of desired metallurgy, mask #7 is used to define metallization pattern 112. A cross-sectional view of the finished structure is shown in FIG. 19.

Bipolar transistors fabricated using the proposed method have the following high performance features:

1. The extrinsic base resistance is dominated by the highly doped layers 108 and 110 and therefore is low. This has been achieved without lowering the breakdown voltage and increasing the capacitance of the emitter-base junction as it would be the case if the extrinsic base region had been uniformly doped to the same level of the layers 108 and 110.

2. The intersection of the highly doped buried layers 108 and 110 with the surface acts as a channel stopper to prevent surface leakage between collector 98 and emitter 96.

3. In step 11C, SiO₂ layer 104 was grown to insure that the subsequent implant of step 12C did not compensate the doping of the emitter 96 or the active base region 85. However, a beneficial effect can be derived from increasing the doping of the active base region 85 at its edges by the lateral spread of the implanted buried layers 108 and 110. The corresponding reduction of the sheet resistance of the active base around its periphery will counteract the nonuniform voltage distribution that arises along the base 85 at high current densities; the so-called emitter crowding effect. The lateral base current flow reduces the emitter-base forward bias from its maximum at the outer edges. The voltage gradient is greatest at the edges where the base current is at its maximum. Therefore, by reducing the sheet resistance near the edges, the voltage gradient is also reduced since the base current drive is externally fixed. A reduction of emitter crowding increases the collector current at which the current gain or beta starts to fall off.

In summary, a method to fabricate asymmetrical buried layers with abrupt edges has been described. A lift-off technique is used to fabricate a mask with near-vertical edges which delineates the abrupt edges of the buried layers. The introduction of this method into fabrication processes for Schottky barrier FETs and bipolar transistors yield buried layers whose abrupt edges are self-aligned with respect to the active regions of the device. Several electrical characteristics are improved by using these layers. For the Schottky barrier FET, the improvements are:

1. Reduced source-gate region and drain-gate region parasitic resistance,

2. Reduced interelectrode capacitance and

3. Larger interelectrode breakdown voltage.

For the bipolar transistor, the improvements are:

1. Reduced extrinsic base resistance without lowering the breakdown voltage and increasing the emitter-base sidewall capacitance,

2. channel stopper in the base region of the emitter-base junction and

3. reduction of emitter crowding effect.

Since the improved characteristics are associated with high performance devices, the need for an electron beam exposure system fits naturally into the fabrication process.

While the invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in form and details can be made therein without departing from the spirit and scope of the invention. 

I claim:
 1. In a semiconductor device, an asymmetrical, buried, conductive layer beneath the surface of a semiconductor substrate, comprising:an ion-implanted conductive layer formed in the bulk of the substrate having a first end with an angular contour contacting the surface of the substrate and a second end abruptly terminating within the bulk of said substrate.
 2. The device of claim 1, wherein said semiconductor substrate has a background dopant of a first conductivity type.
 3. The device of claim 2, wherein said ion-implanted dopant is of said first conductivity type;whereby a high conductance buried layer is formed.
 4. The device of claim 2, wherein said ion-implanted dopant is of a second conductivity type opposite said first conductivity type;whereby a buried p-n junction region is formed.
 5. In a Schottky field effect transistor device in a semiconductor substrate of a first conductivity type, a source and drain structure, comprising:ion-implanted source and drain semiconductor structures of said first conductivity type, each having an abrupt, buried end beneath the surface of the substrate separated by a channel region and a second end which gradually slopes upward toward the surface of said substrate.
 6. The device of claim 5, which further comprises:a gate region on the surface of said semiconductor substrate above said channel region, having a Schottky barrier contact therein; whereby a Schottky barrier field effect transistor device is formed.
 7. In a bipolar transistor in a semiconductor substrate of a first conductivity type having an emitter region surrounded by a base region, the base region comprising:ion-implanted semiconductor structures, each having an abrupt, buried end beneath the emitter region of the transistor and a second end which gradually slopes upward toward the surface of said base region; whereby the extrinsic base resistance of the bipolar transistor is reduced. 